Jamplast JPTPUET
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IshoQ4_Jamplast-JPTPUET.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| JPTPUET thermoplastic polyurethane elastomer is a polyester polycaprolactone based polyurethane elastomer which contains UV stabilizers and combines excellent resistance to fuels and oils with good hydrolytic stability compared to other polyester based TPUs. Its typical applications include seals, gaskets, belting, animal ID tags and other fabricated products. |
| General Information | |
|---|---|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (224°C/1.2 kg) | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 1.60 mm | 0.50 to 0.60 | % | |
| Across Flow : 1.60 mm | 0.50 to 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 86 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-22 Wheel) | 50.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 50% Strain | 5.86 | MPa | |
| 100% Strain | 7.24 | MPa | |
| 300% Strain | 15.2 | MPa | |
| Tensile Strength (Break) | 40.3 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 530 | % | ASTM D412 |
| Tear Strength 1 | 91.1 | kN/m | ASTM D624 |
| Compression Set (25°C, 22 hr) | 25 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -37.2 | °C | DSC |
| Vicat Softening Temperature | 92.2 | °C | ASTM D1525 |
| CLTE - Flow | 1.5E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 199 to 210 | °C | |
| Mold Temperature | 15.6 to 60.0 | °C | |
| Injection Pressure | 41.4 to 103 | MPa | |
| Back Pressure | 0.00 to 0.689 | MPa | |
| Screw Speed | 50 to 75 | rpm | |
| Clamp Tonnage | 4.1 to 6.9 | kN/cm² | |
| Screw L/D Ratio | 18.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 to 3.5:1.0 |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STYRON™ 498 | Americas Styrenics LLC | PS (HIPS) | STYRON™ |
| Ultraform® S 2320 003 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| LEXAN™ HFD4413 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Wanthane® WHT-1185N | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Sylvin 9302-70 FU WHITE 184 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |