SURPASS® RMs539-U(UG)

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	NOVA Chemicals
Trademark:	SURPASS®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	IsIp6u_SURPASS-RMs539-U-UG-.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

SURPASS® RMs539-U(UG) is a Linear Low Density Polyethylene material. It is available in North America for compression molding or rotational molding.

Important attributes of SURPASS® RMs539-U(UG) are:

Flame Rated

Antioxidant

Copolymer

Fast Molding Cycle

Food Contact Acceptable

Typical applications include:

Food Contact Applications

Plumbing/Piping/Potable Water

Containers

Marine Applications

Sporting Goods

General Information
Additive	Antioxidant UV Stabilizer
Features	Antioxidant Copolymer Fast Molding Cycle Food Contact Acceptable Good Mold Release Good Processability Good Stiffness Low Density Low Temperature Impact Resistance Low Viscosity Octene Comonomer Pleasing Surface Appearance
Uses	Containers Marine Applications Septic Tanks Sporting Goods
Agency Ratings	FDA 21 CFR 176.170(c), Table 2, Cond. B FDA 21 CFR 176.170(c), Table 2, Cond. C FDA 21 CFR 176.170(c), Table 2, Cond. D FDA 21 CFR 176.170(c), Table 2, Cond. E FDA 21 CFR 176.170(c), Table 2, Cond. F FDA 21 CFR 176.170(c), Table 2, Cond. G FDA 21 CFR 176.170(c), Table 2, Cond. H FDA 21 CFR 177.1520(c) 3.2a NSF 24 NSF 51 NSF 61
Forms	Pellets
Processing Method	Compression Molding Rotational Molding

Physical	Nominal Value	Unit	Test Method
Density	0.939	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	5.2	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance
50°C, 100% Igepal, Compression Molded, F50	> 1000	hr	ASTM D1693A
50°C, 100% Igepal, Compression Molded, F50	> 1000	hr	ASTM D1693B

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, 1.90 mm, Compression Molded)	20.0	MPa	ASTM D638
Tensile Elongation ²(Yield, 1.90 mm, Compression Molded)	13	%	ASTM D638
Flexural Modulus - 1% Secant (Compression Molded)	780	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Low Temperature Impact - Rotational Molded			ARM
-40°C, 3.18 mm	54.0	J
-40°C, 6.35 mm	230	J

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed, Compression Molded	60.0	°C
1.8 MPa, Unannealed, Compression Molded	42.0	°C
Melting Temperature	125	°C	DSC

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Note Message
1 .	Type IV, 51 mm/min
2 .	Type IV, 51 mm/min

Resin Grade	Manufacturer	Category	Trademark
RTP 102 CC HI	RTP Company	PP, Unspecified	RTP
Geon™ Vinyl Flexible XV3844	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
KOPLA PA66 KDE1020	KOPLA Co., Ltd.	Nylon 66	KOPLA PA66
Sumiliteresin® PR-51618G	SBHPP	Phenolic	Sumiliteresin®
PENTAMID B natural (dryblend)	PENTAC Polymer GmbH	Nylon 6	PENTAMID B