Shuang-Bang AB-120OKA

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	Shuang-Bang Industrial Corp.
Trademark:	Shuang-Bang
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Is5F8G_Shuang-Bang-AB-120OKA.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
One component PU Resins PU membrane is produced by coating the resin on substrate and drying it to vaporize the solvent adequately. The membrane gives soft hand-feel and dry surface, and offers waterproof and windproof properties. Using one component type PU resin alone with adequate crosslinker for yarn fixation, following by drying process to vaporize solvent adequately, could form high yarn-bonding membrane. Shoes, leather bag, ready-make clothes Blocking resistance, high water resistance, good hand-feel Waterproof soft resin. Excellent adhesive strength with PU or PVC, weather resistance, water pressure resistance, and blocking resistance

Message

One component PU Resins

PU membrane is produced by coating the resin on substrate and drying it to vaporize the solvent adequately. The membrane gives soft hand-feel and dry surface, and offers waterproof and windproof properties. Using one component type PU resin alone with adequate crosslinker for yarn fixation, following by drying process to vaporize solvent adequately, could form high yarn-bonding membrane.

Shoes, leather bag, ready-make clothes

Blocking resistance, high water resistance, good hand-feel

Waterproof soft resin. Excellent adhesive strength with PU or PVC, weather resistance, water pressure resistance, and blocking resistance

General Information
Features	Crosslinkable Good Adhesion Good Weather Resistance Moisture Resistant Soft
Uses	Adhesives Coating Applications Footwear
Appearance	Clear/Transparent Transparent - Slight Yellow

Additional Information	Nominal Value	Unit
Solvents	DMF/TOL

Uncured Properties	Nominal Value	Unit
Color	Clear/Transparent Colorless Clear, Light Yellow
Solids Content	27 to 29	%
Viscosity (25°C)	50 to 80	Pa·s

Cured Properties	Nominal Value	Unit
Tensile Modulus (100% Secant)	1.96 to 3.92	MPa
Tensile Strength	> 17.7	MPa
Tensile Elongation at Break	> 500	%

Resin Grade	Manufacturer	Category	Trademark
Maxelast® F02-137B	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
RTP 1083	RTP Company	PBT	RTP
Sasol Polymers PE LT033 (Film Extrusion)	Sasol Polymers	LDPE	Sasol Polymers PE
Nypol® PA A3 G38 HS UV RH PRTA011 NR447	Petropol Industry and Trade of Polymers LTDA	Nylon 66	Nypol® PA
Nycal™ 2155R33	Technical Polymers, LLC	Nylon 66	Nycal™