SABIC® HDPE PCG5421
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IqXnZY_SABIC-HDPE-PCG5421.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCG5421 is typically used for the blow moulding of healthcare packaging (bottles and cans). The product features a good stiffness/ESCR balance combined with good process ability. Compliance to regulations SABIC® HDPE PCG5421 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.16 | g/10 min | |
| 190°C/21.6 kg | 20 | g/10 min | |
| 190°C/5.0 kg | 0.89 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(75°C, 1.00 mm, Rhodacal-DS10, Compression Molded) | 16.0 | hr | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1050 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 26.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 27.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1250 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 27.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Compression Molded | 6.0 | kJ/m² | |
| 23°C, Compression Molded | 14 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 81.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 127 | °C | ISO 306/A |
| Melting Temperature (DSC) | 132 | °C | ISO 11357-3 |
| Enthalpy Change | 205 | J/g | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 3 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Synthos EPS® 0308F/PL | Synthos S.A. | PS (EPS) | Synthos EPS® |
| Fainplast PVC RKS 710/W | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| FHR EPS 54-7654 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Hylex® P1010G30FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| apigo bio® PM 120 | API SpA | TPO (POE) | apigo bio® |