CP PRYME® Polycarbonate PC100RUL-18M Clear
| Category: | PC , Polycarbonate |
| Manufacturer: | Chase Plastics Services Inc. |
| Trademark: | CP PRYME® Polycarbonate |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Iq7Uso_CP-PRYME-Polycarbonate-PC100RUL-18M-Clear.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CP PRYME® Polycarbonate PC100RUL-18M Clear is a Polycarbonate (PC) product. It is available in North America. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Specific Volume | 0.835 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.15 | % | |
| Equilibrium, 23°C | 0.35 | % | |
| Equilibrium, 100°C | 0.58 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 70 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 62.1 | MPa | |
| Break | 68.9 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 130 | % | |
| Flexural Modulus 3(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 96.5 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| Charpy Unnotched Impact Strength 6 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| 23°C | 690 | J/m | ASTM D256 |
| -30°C 7 | 11 | kJ/m² | ISO 180/1A |
| 23°C 8 | 65 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 3200 | J/m | ASTM D256 |
| -30°C 9 | No Break | ISO 180/1U | |
| 23°C 10 | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 62.1 | J | ASTM D3763 |
| Gardner Impact (23°C) | 169 | J | ASTM D3029 |
| Tensile Impact Strength 11 | 546 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 138 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 129 | °C | |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 12 |
| CLTE - Flow (-40 to 95°C) | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1260 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM C177 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 80*10*3 sp=62mm |
| 6 . | 80*10*3 sp=62mm |
| 7 . | 80*10*3 |
| 8 . | 80*10*3 |
| 9 . | 80*10*3 |
| 10 . | 80*10*3 |
| 11 . | Type S |
| 12 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® B220MN | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| Sindustris PP HM3208SM | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| NORYL™ 6850C resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |
| LUVOCOM® 1850-8384 | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| Petrothene® LP510031 | LyondellBasell Industries | HDPE | Petrothene® |