DENKA ABS GR-2000
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IpxEnN_DENKA-ABS-GR-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DENKA ABS GR-2000 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| 23°C | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 117 | ASTM D785 | |
| R-Scale | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 47.0 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 50.0 | MPa | |
| Break | 35.0 | MPa | |
| Nominal Tensile Strain at Break | 27 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2500 | MPa | ASTM D790 |
| -- 3 | 2550 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 75.0 | MPa | ASTM D790 |
| -- 5 | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 23 | kJ/m² | ISO 179 |
| Notched Izod Impact | 230 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 6 | 90.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 81.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 102 | °C | ISO 306/B, ASTM D1525 7 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 8 | > 1.0E+16 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 210 to 260 | °C | |
| Nozzle Temperature | 210 to 255 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 0.490 to 0.981 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 15 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 15 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Edgewise |
| 7 . | Loading 2 (50 N) |
| 8 . | 23°C, 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Andur 8-5 APLS/Curene® 49 | Anderson Development Company | PUR-Ester/TDI | Andur |
| HiFill FR® PA4/6 FR | Techmer Engineered Solutions | Nylon 46 | HiFill FR® |
| Hostacom EKC 330N E1 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| LNP™ LUBRICOMP™ DFL36XXJ compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Petrothene® GA818073 | LyondellBasell Industries | LLDPE | Petrothene® |