MACOMASS PP MM-PP HI 22
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | MACOMASS Verkaufs AG |
| Trademark: | MACOMASS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IpGaEn_MACOMASS-PP-MM-PP-HI-22.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MACOMASS PP MM-PP HI 22 is a Polypropylene Homopolymer (PP Homopolymer) material filled with 40% talc. It is available in Europe. Primary attribute of MACOMASS PP MM-PP HI 22: Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 to 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 to 17 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 86.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 132 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 83.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | |
|---|---|---|---|
| Glow Wire Ignition Temperature | |||
| 1.60 mm | 750 | °C | |
| 3.20 mm | 750 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DJSilicone NE-641 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Fainplast PVC PMP 75/OP | Fainplast Compounds S.r.l | PVC+PUR | Fainplast PVC |
| Fortron® 6341L4 | Celanese Corporation | PPS | Fortron® |
| PHOENIX™ 16601 | Phon Tech Industrial Company | TPV | PHOENIX™ |
| Durethan® B 35 FKA 000000 | LANXESS GmbH | Nylon 6 | Durethan® |