Reny® 2686
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IogvDw_Reny-2686.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reny® 2686 is a Polyarylamide (PARA) material filled with 65% glass bead. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 2686: Warp Resistant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.80 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 7.6 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 6.90 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.87 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.11 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.70 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9800 | 7300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 73.0 | 52.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.7 | 1.8 | % | ISO 527-2 |
| Flexural Modulus | 9600 | 6600 | MPa | ISO 178 |
| Flexural Stress | 147 | 103 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.2 | 2.4 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 32 | 40 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 213 | 207 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 147 | 116 | °C | ISO 75-2/A |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 CFGV 15/15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Formolon® KVF | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| Hanwha Total PP EB42 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Lucent PC PC-1418FD | Lucent Polymers, Inc. | PC | Lucent PC |
| POLYblend PC/ABS 85FS GF10 | Polykemi AB | PC+ABS | POLYblend |