TECACOMP® PPS TRM PVX black 4008
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IoaTsn_TECACOMPPPSTRMPVXblack4008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (316°C/2.16 kg) | 45 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (316°C/2.16 kg) | 35.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.58 | % | ISO 294-4 |
| Flow | 0.21 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12500 | MPa | ISO 527-2/50 |
| Tensile Stress | 130 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 15 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 285 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 270 | °C | ISO 75-2/A |
| Glass Transition Temperature | 90.0 | °C | DIN 53765 |
| Melting Temperature | 280 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 4.9E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 0.50 | W/m/K | DIN EN 821 |
| -- 2 | 0.90 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 230 | °C | |
| short term | 260 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+5 | ohms·cm | ISO 3915 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 300 - 350 | °C | |
| Mold Temperature | 140 - 160 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SL645 | INDELPRO, S.A. de C.V. | PP Impact Copolymer | Pro-fax |
| BJB Polyurethane TC-816 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Karina CLEAR PVC COMPOUND -E 80/296-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PA6/6 GF40 TL10 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Politen® ESP185 | ITEN INDUSTRIES | Polyester Alloy | Politen® |