Ravago Compounds PP-8162
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ravago Manufacturing Americas, LLC |
| Trademark: | Ravago Compounds |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IoW0x8_Ravago-Compounds-PP-8162.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP-8162 is an injection molding grade polypropylene compound designed for outdoor applications. It combines excellent moldability with outstanding resistance to weathering and sunlight. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 17.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 10 | % | ASTM D638 |
| Flexural Modulus - Tangent 1(23°C) | 1030 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Dart Drop Impact 2 | 14.7 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 101 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 57.2 | °C | ASTM D648 |
| CLTE - Flow | 7.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 17 | mm/min | ASTM D635 |
| Self Ignition Temperature | 427 | °C | ASTM D1929 |
| Smoke Density | 6.0 | % | ASTM D2843 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 93.3 | °C | |
| Drying Time | 0.0 - 8.0 | hr | |
| Rear Temperature | 177 - 216 | °C | |
| Middle Temperature | 177 - 216 | °C | |
| Front Temperature | 171 - 216 | °C | |
| Nozzle Temperature | 182 - 216 | °C | |
| Mold Temperature | 26.7 - 60.0 | °C | |
| Back Pressure | 0.00 - 0.689 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Injection instructions |
|---|
| Hot Runner Temperature (if applicable): 450 to 480°F |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | Geometry GC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS-351T | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Chemiton GTB5FA 80E | Franplast S.r.l. | SEBS | Chemiton |
| Epic Epoxy S7292 | Epic Resins | Epoxy | Epic Epoxy |
| Iupilon® EGN2020BR | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LNP™ THERMOCOMP™ IF006 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |