Braskem PE SHA7260
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IlWs8g_Braskem-PE-SHA7260.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SHA7260 is a high-density polyethylene, developed for the injection molding, easy to process and with high productivity. This resin has a good melt flow with high rigidity and hardness. Its narrow molar mass distribution results in a low tendency to warpage. The minimum biobased content of this grade is 94.5%, determined according to ASTM D6866. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.955 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1(50°C, 2.00 mm, 100% Igepal, Compression Molded, F50) | < 4.00 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Compression Molded) | 29.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Compression Molded) | 7.2 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 1350 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 74.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 95 | % | ASTM D6866 |
| Note Message | |
|---|---|
| 1 . | 0.3 mm notched-plaques |
| 2 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx TPP2B10 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| TRIEL® 5402EM | Samyang Corporation | TPEE | TRIEL® |
| AKROMID® A3 ICF 30 black (5021) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| HAIPLEN H30 G4 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| KEBAFLEX® SG 95 A.01 black | BARLOG plastics GmbH | TES | KEBAFLEX® |