InnoClear™ OC-5050
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoClear™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IkQw5n_InnoClear-OC-5050.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OC-5050 is a water clear, semi-flexible polyurethane elastomer formulated for room temperature hand-batch or vacuum assisted processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA,or TDI. OC-5050 has low viscosity and uses materials that have excellent U.V. resistant qualities. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.07 | g/cm³ | |
| Base Resin | 1.07 | g/cm³ | |
| Hardener | 1.10 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 50 Mix Ratio by Volume: 51 | ||
| Demold Time | 960 to 1400 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.50 | Pa·s | |
| 25°C 2 | 0.65 | Pa·s | |
| 25°C 3 | 1.0 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 15 to 25 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 45 to 55 | ASTM D2240 | |
| Tensile Strength | 1.55 | MPa | ASTM D638 |
| Tensile Elongation at Break | 65 | % | ASTM D638 |
| Tear Strength | 7.01 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1472 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 285H TFE 15 | RTP Company | Nylon 66 | RTP |
| Wellamid® FR22F-NBK3 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| FRblend® PC-1303 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC | FRblend® |
| LNP™ VERTON™ RV00AE compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |