Tarnamid® T-27 GF 15AT
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IkQBeE_Tarnamid-T-27-GF-15AT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| It is reinforced polyamide 6 compound, heat stabilised. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 45.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (2.00 mm) | 0.50 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 220 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7600 | -- | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 105 | -- | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | -- | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6000 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 150 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 35 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 3.5 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 190 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | -- | °C | ISO 306/B |
| Melting Temperature | 221 | -- | °C | ISO 11357-3 |
| Limit of Temperature - a few hours operation | 180 | -- | °C | |
| Temperature Index | ||||
| 20000 hr | 110 | -- | °C | |
| 5000 hr | 120 | -- | °C |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | + | -- | FMVSS 302 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 4.2E+15 | 6.2E+11 | ohms | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.20 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen P 9421 66409 | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® Vestolen P |
| Rilsan® MA 3950 | Arkema | Nylon 12 | Rilsan® |
| TABOREX TA 1109 MD | SILON s.ro | HDPE | TABOREX |
| Fainplast PVC GS 60 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Hanwha Total PP BB150 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |