Generic TPEE
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Iis5vd_Generic-TPEE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPEE This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 - 1.29 | g/cm³ | ASTM D792 |
| 23°C | 1.16 - 1.28 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 - 28 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 1.3 - 1.9 | % | ASTM D955 |
| 23°C | 0.62 - 2.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.45 - 0.51 | % | ASTM D570 |
| 23°C, 24 hr | 0.30 - 0.60 | % | ISO 62 |
| Equilibrium, 23°C | 0.28 - 0.56 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 30 - 99 | ASTM D2240 | |
| 23°C | 40 - 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 50.0 - 523 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 13.9 - 40.7 | MPa | ASTM D638 |
| Yield, 23°C | 2.40 - 40.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 6.86 - 42.2 | MPa | ASTM D638 |
| Fracture, 23°C | 15.0 - 49.0 | MPa | ISO 527-2 |
| 23°C | 2.26 - 27.8 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture, 23°C | 390 - 720 | % | ASTM D638 |
| Fracture, 23°C | 230 - 500 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 15.0 - 307 | MPa | ASTM D790 |
| 23°C | 54.0 - 350 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 9.98 - 12.0 | MPa | ISO 178 |
| Yield, 23°C | 1.77 - 39.2 | MPa | ASTM D790 |
| Compressive Modulus | 2.00 - 39.2 | MPa | ASTM D695 |
| Compressive Strength (23°C) | 2.40 - 39.2 | MPa | ASTM D695 |
| Taber Abrasion Resistance (23°C) | 3.00 - 20.4 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (50% strain, 23°C) | 2.50 - 28.5 | MPa | ASTM D412 |
| Tear Strength (23°C) | 74.3 - 250 | kN/m | ASTM D624 |
| Compression Set | 47 - 65 | % | ASTM D395 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 - 150 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 69 - 580 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 43.0 - 135 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 56.0 - 193 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 25.0 - 147 | °C | ASTM D648 |
| Brittleness Temperature | -65.5 - -65.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 64.7 - 211 | °C | ASTM D1525 |
| Melting Temperature | |||
| -- | 195 - 219 | °C | |
| -- | 171 - 223 | °C | DSC |
| -- | 200 - 218 | °C | ASTM D3418 |
| -- | 204 - 218 | °C | ISO 3146 |
| CLTE - Flow | |||
| -- | 1.4E-4 - 1.7E-4 | cm/cm/°C | ASTM D696 |
| -- | 1.1E-4 - 1.7E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 5.0E+8 - 1.8E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 20 - 30 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 81.5 - 106 | °C | |
| Drying Time | 2.5 - 4.0 | hr | |
| Suggested Max Moisture | 0.079 - 0.10 | % | |
| Rear Temperature | 187 - 221 | °C | |
| Middle Temperature | 209 - 245 | °C | |
| Front Temperature | 232 - 245 | °C | |
| Processing (Melt) Temp | 189 - 231 | °C | |
| Mold Temperature | 35.0 - 40.6 | °C | |
| Screw Speed | 45 - 60 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPEEThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES J-50/10 | Techmer Engineered Solutions | PC | TES |
| ELASTOSIL® P 7616-160 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® P |
| Globalene® 6331F | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| Hostacom ERC 161N G51452 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Moplen HP3065 | LyondellBasell Industries | PP Homopolymer | Moplen |