AZDEL™ C327-B01
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Azdel, Inc. |
| Trademark: | AZDEL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IigA2b_AZDEL-C327-B01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AZDEL C327-B01 is a glass mat thermoplastic laminate based oupon a random oriented chopped fiber mat and material filler contained within a polypropylene resin matrix. This composite material features high flow properties and a very homogeneous fiber distribution into features such as ribs and bosses is desired. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.32 mm) | 0.40 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4530 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2 |
| Flexural Modulus | 4260 | MPa | ISO 178 |
| Flexural Stress | 97.7 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 28 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | ASTM D3763 | ||
| 102 mm, Energy at Failure | 21.4 | J | ASTM D3763 |
| 102 mm, Energy at Max Load | 12.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 160 | °C | ISO 75-2/A |
| CLTE - Flow (-40 to 121°C) | 5.1E-5 | cm/cm/°C | ASTM E831 |
| Additional Information |
|---|
| Specific Gravity, ISO 1183, Laminate: 1.12Specific Gravity, ISO 1183, Molded: 1.15Sheet Thickness, internal: 4.32mmBasis Weight (Mass per unit area), internal: 4.83 kg/m²Poisson's Ratio, ISO 527: 0.428Multiaxial Impact, ASTM D-3763, Force @ max load, 4.0" thickness: 2629 N |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PS-GP1 | Polymer Resources Ltd. | PS (HIPS) | PRL |
| Milastomer™ 5030NHS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| VICOTE® F817 Enhanced | Victrex plc | PEEK | VICOTE® |
| Viton® GLT-600S | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| Karina CLEAR PVC COMPOUND 80/221-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |