Geon™ HTX Ultra LA426 Gray 2382
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IiDg2L_Geon-HTX-Ultra-LA426-Gray-2382.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| It is most suitable for black and darker colors with color values between 50 and 70L. The same applies to colors with color values above 70L. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 4-41410-64-0000 | ASTM D4216 | |
| PVC Cell Classification | 15215 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1900 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 35.2 | MPa | ASTM D638 |
| Flexural Modulus | 1910 | MPa | ASTM D790 |
| Flexural Strength | 61.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 720 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 59.6 | J/cm | ASTM D4226 |
| 23°C 4 | 178 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 90.0 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 91.1 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 83.3 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 86.7 | °C | ASTM D648 |
| CLTE - Flow | 8.4E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Acceptable | ||
| 推荐在华氏160度下将材料干燥至少2小时。物理属性基于 Geon HTX Ultra LA426 Gray 2382 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 174 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA66 ZRPA66 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 66 | Shandong PA66 |
| Tecnoprene® AK7HCT NAT001 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| NORYL™ HM3020H resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| LNP™ VERTON™ NV006E compound | SABIC Innovative Plastics | PC+ABS | LNP™ VERTON™ |
| Optix® CA-82 FDA | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |