Drystar™ 0603
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Drystar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IhMTCd_Drystar-0603.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eastman is pleased to announce the launch of DRYSTAR* copolyesters. This new product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman?s copolyesters are highly valued for their excellent balance of properties such as superior aesthetics, impact strength, and chemical resistance. These properties can be optimally realized when the resins are properly dehydrated in accordance to recommended drying conditions and equipment. Recognizing this value, Eastman conceived Drystar™ copolyesters to allow converters with limited access to desiccant dryers to achieve these optimizations. In addition, some converters with desiccant dryers may still find Drystar™ copolyesters value-adding to attain production flexibility and cost saving by removing the drying process prior to injection molding, profile extruding, or extrusion blow molding copolyesters. The initial launch comprises of the commercialization of four grades of Drystar™ copolyesters and Eastman has on-going program to extend this strategic product-line in the future. *DRYSTAR is only available in the Asia Pacific Region. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2030 | MPa | ASTM D638 |
| 23°C | 2000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 50.0 | MPa | ASTM D638 |
| Yield, 23°C | 48.0 | MPa | ISO 527-2 |
| Break, 23°C | 30.0 | MPa | ASTM D638 |
| Break, 23°C | 29.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 4.4 | % | ASTM D638 |
| Yield, 23°C | 4.0 | % | ISO 527-2 |
| Break, 23°C | 180 | % | ASTM D638 |
| Break, 23°C | 200 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2060 | MPa | ASTM D790 |
| 23°C | 2100 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 68.0 | MPa | ASTM D790 |
| 23°C | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 40 | J/m | ASTM D256 |
| 23°C | 110 | J/m | ASTM D256 |
| -40°C | 4.4 | kJ/m² | ISO 180 |
| 23°C | 9.4 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D4812 | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 70.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.0 | °C | ASTM D648, ISO 75-2/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 90.0 | % | ASTM D1003 |
| Haze | 0.20 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.0 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 16.0 to 38.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ HDPE DMDA-8940 HEALTH+™ | The Dow Chemical Company | HDPE | DOW™ HDPE |
| 3M™ Dyneon™ PTFE Compound TF 6302 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Complet® LGF50-PA12 | PlastiComp, Inc. | Nylon 12 | Complet® |
| HYDEX® 4101L | Ensinger Inc. | Polyester, TP | HYDEX® |
| ASPIRE VINYL™ G820 | Axiall Corporation | PVC, Flexible | ASPIRE VINYL™ |