VESTAMID® NRG 6001 natural color
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® NRG |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IgsIw1_VESTAMID-NRG-6001-natural-color.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High viscosity, platicized, impact-modified, heat and light stabilized PA12 compound for extrusion. VESTAMID®NRG 6001 natural color is a plasticized PA 12 compound with heat and light stabilizers for the extrusion of flexible tubing and hoses especially for oil and petrochemical applications. VESTAMID®NRG 6001 natural color is characterized by easy processing and good dimensional control during pipe extrusion, especially when processing large pipe diameters. Properties of compounds based on polyamide 12 vary little with changing humidity due to low moisture absorption Parts made of the described semi-crystalline materialare characterized by exceptional impact strength, low coefficient of sliding friction and good chemical resistance. VESTAMID®NRG 6001 is supplied ready for use in moisture-proof bags. The recommended process temperature for extrusion is 220°C to 260°C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.02 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 390 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield 1 | 26.0 | MPa | |
| Break | 44.0 | MPa | |
| Tensile Strain 2 | |||
| Yield | 30 | % | ISO 527-2 |
| Break | > 150 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| Partial Break | 94 | kJ/m² | |
| -40°C, Complete Break | 5.4 | kJ/m² | |
| -30°C, Complete Break | 7.2 | kJ/m² | |
| 23°C, Partial Break | 130 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | No Break | ||
| -30°C | No Break | ||
| 0°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 118 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 164 | °C | ISO 306/A |
| -- | 124 | °C | ISO 306/B |
| Melting Temperature 3 | 172 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Hoop Stress - at burst (23°C) | 23.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 260 | °C |
| Note Message | |
|---|---|
| 1 . | Pipe Test Specimen |
| 2 . | Pipe Test Specimen |
| 3 . | 2nd Heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BZM 30 TL | Arkema | Nylon 11 | Rilsan® |
| RTP 300 HF Z | RTP Company | PC | RTP |
| TRIEL® 5750 | Samyang Corporation | TPEE | TRIEL® |
| Zytel® RS LC3090 NC010 | DuPont Performance Polymers | Nylon 610 | Zytel® RS |
| Borlink™ LE0511 | Borealis AG | PE, Unspecified | Borlink™ |