Hifax CB259
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IgpNgr_Hifax-CB259.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hifax CB259 medium high melt flow, 1,600 MPa flexural modulus, low CLTE, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good balance of impact resistance, rigidity and dimensional stability. It was designed for exterior ornamentation applications requiring stiffness and low thermal expansion characteristics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield | 8.0 | % | ISO 527-2 |
| Break, 23°C | 400 | % | ISO 527-2/50 |
| Flexural Modulus | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 3.0 | kJ/m² | |
| 23°C | 33 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 94.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 53.0 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 100°C) | 4.9E-5 | cm/cm/°C | ASTM E228, ISO 11359-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-5530U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Electrafil® J-80/CF/10/Natl | Techmer Engineered Solutions | Acetal (POM) Copolymer | Electrafil® |
| Latiblend 5262 | LATI S.p.A. | Nylon+PP | Latiblend |
| Lupox® GP1000W | LG Chem Ltd. | PBT | Lupox® |
| Moplen HP622J | LyondellBasell Industries | PP Homopolymer | Moplen |