LNP™ THERMOCOMP™ IF008 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Igomz8_LNPTHERMOCOMPIF008compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* IF008 is a compound based on Nylon 6/12 resin containing 40% Glass Fiber. Also known as: LNP* Thermocomp* Compound IF-1008 Product reorder name: IF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 176 | MPa | ASTM D638 |
| Flexural Modulus | 10600 | MPa | ASTM D790 |
| Flexural Strength | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 199 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Rear Temperature | 254 - 266 | °C | |
| Middle Temperature | 260 - 271 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 271 - 277 | °C | |
| Mold Temperature | 66 - 93 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® N 2200 G43 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| DOW™ LDPE 545E | The Dow Chemical Company | LDPE | DOW™ LDPE |
| Fainplast PVC MPH 75/T | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| ELASTOSIL® E 70 | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| HAIPLEN EP70 C8 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |