LUVOCOM® 1850-8654 Datasheet,PBT,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®1850-8654 is a polybutene terephthalate (PBT) material, which contains a glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1850-8654 are: Conductivity anti-warping Good stiffness Typical application areas include: Electrical/electronic applications textile/fiber engineering/industrial accessories Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Heat conduction Low warpage Rigid, good Good strength
Uses	Electrical/Electronic Applications Textile applications Engineering accessories Application in Automobile Field Business equipment
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.67	g/cm³	ISO 1183
Molding Shrinkage	0.30 - 0.70	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	14000	MPa	ISO 527-2
Tensile Stress (Break)	98.0	MPa	ISO 527-2
Tensile Strain (Yield)	1.2	%	ISO 527-2
Flexural Modulus	11000	MPa	ISO 178
Flexural Stress	150	MPa	ISO 178
Flexural Strain at Flexural Strength	1.6	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	180	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+13	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	22	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	130	°C	UL 746B
Thermal Conductivity ¹	3.5	W/m/K

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+13	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	120	°C
Vacuum dryer, B	80	°C
Drying Time
Hot air dryer, A	4.0 - 6.0	hr
Vacuum dryer, B	6.0 - 8.0	hr
Rear Temperature	240 - 260	°C
Middle Temperature	260 - 280	°C
Front Temperature	250 - 270	°C
Nozzle Temperature	250 - 265	°C
Processing (Melt) Temp	250	°C
Mold Temperature	60 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Note Message
1 .	Hot-Disk, 60x60x3 mm

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	IgXlF2_LUVOCOM18508654.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Braskem PE SLH218	Braskem	LLDPE	Braskem PE
ESTAPROP 0540 GFC V0	Cossa Polimeri S.r.l.	PP, Unspecified	ESTAPROP
Delta N66-1800 HSL	Delta Polymers	Nylon 66	Delta
Honeywell PCTFE P7500HS	Honeywell	PCTFE	Honeywell PCTFE
KYOCERA KE-300AH	KYOCERA Chemical Corporation	Epoxy	KYOCERA