Bergamid™ Bergamid™ A65 GK15 natur SOx
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ig2Olc_Bergamid-Bergamid-A65-GK15-natur-SOx.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bergamid™ Bergamid™ A65 GK15 natur SOx is a Polyamide 66 (Nylon 66) product filled with 15% glass bead. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1(23°C) | 1.23 | g/cm³ | DIN 53479 |
| Molding Shrinkage 2(23°C, 4.00 mm) | 1.4 to 1.9 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 3(23°C, 4.00 mm, Injection Molded) | 4100 | MPa | ISO 527-2/1 |
| Tensile Stress 4(Break, 23°C, 4.00 mm, Injection Molded) | 60.0 | MPa | ISO 527-2/5 |
| Tensile Strain 5(Break, 23°C, 4.00 mm, Injection Molded) | 1.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C, Injection Molded | 1.4 | kJ/m² | ISO 179 |
| 23°C 6 | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | |||
| -30°C, Injection Molded | 15 | kJ/m² | ISO 179 |
| 23°C, Injection Molded 7 | 15 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 224 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.5 | °C | ISO 75-2/A |
| Maximum Use Temperature | |||
| long term (GTP 50% tensile) | 85 | °C | IEC 216 |
| short time | 180 | °C | IEC 60216 |
| Melting Temperature (DSC) | 261 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | IEC 93 | ||
| -- 8 | 1.0E+10 | ohms | |
| -- 9 | 1.0E+13 | ohms | |
| Volume Resistivity | IEC 93 | ||
| -- 10 | 1.0E+12 | ohms·cm | |
| -- 11 | 1.0E+15 | ohms·cm | |
| Dissipation Factor 12(1 MHz) | 1.0E-4 | IEC 60250 | |
| Comparative Tracking Index 13(Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | ±0.03 |
| 2 . | Bergmann method |
| 3 . | dry |
| 4 . | dry |
| 5 . | dry |
| 6 . | dry |
| 7 . | dry |
| 8 . | air humidity |
| 9 . | dry |
| 10 . | air humidity |
| 11 . | dry |
| 12 . | air humidity |
| 13 . | dry |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 HB | RTP Company | Nylon 66 | RTP |
| Shin-Etsu RTV KE-3472T | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Sylvin 2910-65LG Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Toraypef® 20015 AP16 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| Bergamid™ B70 G30 H white VN8080CF UV | PolyOne Corporation | Nylon 6 | Bergamid™ |