Daplen™ EF150HP
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Daplen™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IfyLqO_Daplen-EF150HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daplen EF150HP is an elastomer modified polypropylene compound intended for injection moulding. This material has excellent balanced mechanical properties, gives a good surface quality and is easy to process. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress | 29.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 4.5 | kJ/m² | ISO 179/1eA |
| 23°C | 29 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 75 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 4.3 | kJ/m² | ISO 180/1A |
| 23°C | 25 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/Be |
| 1.8 MPa, not annealed | 57.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 136 | °C | ISO 306/A |
| -- | 50.0 | °C | ISO 306/B |
| CLTE - Flow | 5.4E-5 | cm/cm/°C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperatrue: 40 - 80 °CMass Temperature: 220 - 260 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylfor® A2 FR2/3A NATURALE | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| BITONER® C9 H-100 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| CERTENE™ HR-242U | Muehlstein | HDPE | CERTENE™ |
| Estane® R195A-9 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Sylvin 9077-70 Grey 9511 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |