LNP™ THERMOCOMP™ UC006XXH compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IfDEpD_LNP-THERMOCOMP-UC006XXH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* UC006XXH is a compound based on Polyphthalamide resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare. Also known as: LNP* THERMOCOMP* Compound UC-1006 HC Product reorder name: UC006XXH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.62 | % | ISO 294-4 |
| Flow : 24 hr | 0.16 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.31 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.66 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 26100 | MPa | ASTM D638 |
| -- | 28200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 287 | MPa | ASTM D638 |
| Break | 263 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.5 | % | ASTM D638 |
| Break | 1.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 22600 | MPa | ASTM D790 |
| -- | 22300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 420 | MPa | ASTM D790 |
| -- | 413 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.27 | ||
| vs. Itself - Static | 0.21 | ||
| Wear Factor - Washer | 6.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 2 | 6.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 830 | J/m | ASTM D4812 |
| 23°C 3 | 52 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.91 | J | ASTM D3763 |
| -- | 2.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 286 | °C | ASTM D648 |
| CLTE | |||
| Flow : -40 to 40°C | 1.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J227T | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| Tecomid® NA40 GR40 NL RM | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| Sarlink® TPE FM-2676 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| SQUARE® LSR2034-65BS | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| Sylvin 9067-65 Orange 592 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |