Ultradur® B 4040 G10 BK5110
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IevCTB_Ultradur-B-4040-G10-BK5110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultradur B 4040 G10 BK5110 is a pigmented black, injection molding PBT with 50% glass fiber reinforced for technical parts with excellent surface finish. Applications Typical applications include automotive exterior, door handles, exterior mirror housings, rear screen, wiper arms. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.73 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | |
| Water Absorption | |||
| Saturation | 0.40 | % | ASTM D570 |
| Saturation, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 50% RH | 0.12 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 97.0 | ml/g | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 16500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Break, 23°C | 140 | MPa | ASTM D638 |
| Break, 23°C | 155 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 1.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 13600 | MPa | ASTM D790 |
| 23°C | 15000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 225 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 8.5 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 69 | kJ/m² | |
| 23°C | 52 | kJ/m² | |
| Notched Izod Impact | |||
| -40°C | 64 | J/m | ASTM D256 |
| 23°C | 75 | J/m | ASTM D256 |
| -40°C | 8.1 | kJ/m² | ISO 180 |
| 23°C | 8.2 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 221 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Peak Melting Temperature | 223 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| 1.50 mm | 1.0E+13 | ohms | ASTM D257 |
| -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 1.50 mm | > 1.0E+15 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 4.00 | ||
| 1 MHz | 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.2E-3 | ||
| 1 MHz | 0.015 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | < 1.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PureTherm® 1001C UV | Tekni-Films, a div of Tekni-Plex | Film, PVC | PureTherm® |
| Shandong PA1212 PA1212BR-III | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Nycal™ 1850 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| INEOS PP R35C-01 | INEOS Olefins & Polymers USA | PP Random Copolymer | INEOS PP |
| LEXAN™ OQ4005 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |