EVAL™ E171
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ierubo_EVAL-E171.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
44 mol% Ethylene Vinyl Alcohol Copolymer E171B - Pellets are lubricated to facilitate material feeding into extruder |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 1.7 | g/10 min | |
| 210°C/2.16 kg | 3.3 | g/10 min | |
| Ethylene Content | 44.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 74 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 17 | % | ISO 527-2 |
| Flexural Modulus | 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 0% RH | 0.028 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 0.030 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.066 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 1(40°C, 90% RH) | 0.83 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 2.0 | kJ/m² | ISO 179/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 54.0 | °C | ISO 11357-2 |
| Melting Temperature | 165 | °C | ISO 11357 |
| Peak Crystallization Temperature | 144 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V946 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| 3M™ Dyneon™ PTFE Compound TF 6220 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| ElectriPlast® EP-CF/ABS | Integral Technologies, Inc. | ABS | ElectriPlast® |
| Hifax HSBM CB 1151 G Black | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Osterlene® CIEB-4-00-h | Osterman & Company | PS (GPPS) | Osterlene® |