Surlyn® 1855
| Category: | Ionomer , Ionomer |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Surlyn® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Iecg5o_Surlyn-1855.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Surlyn®1855 is an ionomer (Ionomer) material,. This product is available in North America or Europe. The processing methods are: blown film, co-extrusion or cast film. Surlyn®The main features of the 1855 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.938 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 159 | MPa | ASTM D882 |
| 1% secant, TD | 152 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 36.5 | MPa | ASTM D882 |
| TD : Fracture | 35.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 350 | % | ASTM D882 |
| TD : Fracture | 350 | % | ASTM D882 |
| Dart Drop Impact | 700 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 38 | g | ASTM D1922 |
| TD | 50 | g | ASTM D1922 |
| Water Vapor Transmission | 16 | g/m²/24 hr | ASTM E96 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 62.2 | °C | ASTM D1525 |
| Melting Temperature | 87.8 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 4.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Ion Type: Zinc |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 | °C | |
| Cylinder Zone 2 Temp. | 177 | °C | |
| Cylinder Zone 3 Temp. | 204 | °C | |
| Cylinder Zone 4 Temp. | 204 | °C | |
| Cylinder Zone 5 Temp. | 204 | °C | |
| Melt Temperature | 204 - 227 | °C | |
| Die Temperature | 204 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC RKS 310/K1 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Forprene® 6NM901A45 | SO.F.TER. SPA | TPV | Forprene® |
| Jamplast JPPCGP | Jamplast, Inc. | PC | Jamplast |
| Karina BLACK PVC COMPOUND 105900-48/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ LUX9610 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |