ElectriPlast® EP-CF/PBT
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Integral Technologies, Inc. |
| Trademark: | ElectriPlast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IeFCCi_ElectriPlast-EP-CF-PBT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ElectriPlast®EP-CF/PBT is a polybutene terephthalate (PBT) product, which contains nickel-plated carbon fiber. It can be processed by injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3720 | MPa | ASTM D638 |
| Tensile Strength (Break) | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.78 | % | ASTM D638 |
| Flexural Modulus | 8710 | MPa | ASTM D790 |
| Flexural Strength | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 216 | °C | ASTM D648 |
| CLTE - Flow | 2.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 2.7 | W/m/K | ASTM D5470 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 30 | ohms | ESD STM11.11 |
| Volume Resistivity | 7.5E+2 | ohms·cm | ASTM D257 |
| Static Decay | 10 | msec | Internal method |
| Surface Resistance | 300 | ohms | ESD STM11.11 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 27 | mm/min | UL 94 |
| Flame Rating 1 | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 6.0 | hr | |
| Rear Temperature | 232 | °C | |
| Middle Temperature | 238 | °C | |
| Front Temperature | 243 | °C | |
| Nozzle Temperature | 243 | °C | |
| Back Pressure | 5.52 | MPa | |
| Screw Speed | 100 | rpm |
| Injection instructions |
|---|
| Injection Speed: 2 in/sec1st Stage (injection): 2000 psiDecomposition: 0.5 inch |
| Note Message | |
|---|---|
| 1 . | 27 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® Marine-Tec | Röchling Engineering Plastics SE & Co. KG | TP, Unspecified | POLYSTONE® |
| Enviramid® N2315HL BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |
| HANWHA EVA 1528 | Hanwha Chemical | EVA | HANWHA EVA |
| Latilon 28D K/40 | LATI S.p.A. | PC | Latilon |
| SIBUR Synthetic Rubber SSBR-2560 TDAE Grade C | SIBUR | SBR, Solution | SIBUR Synthetic Rubber |