POLIGOM R/75 C
| Category: | EPDM , Ethylene Propylene Diene Terpolymer |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | POLIGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IdmohR_POLIGOM-R-75-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLIGOM : is the trade-mark of our crosslinkable EPDM/EPR/HEPR compound. POLIGOM R/75 C : chemically crosslinkable rubber for low voltage cable insulation and sheathing suitable for G7. It is a conveniently grafted compound able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/202 or MAC/203. REACTION BETWEEN GRAFTING AND CATALYST: These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 94/6 Certify : CEI 2011 G7,IEC 60502-1 HEPR |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 1.0 - 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 93 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | > 14.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 700 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (150°C, 168 hr) | -15 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (150°C, 168 hr) | -20 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811 | ||
| 250°C | 60 | % | IEC 60811 |
| Residual : 250°C | 0.0 | % | IEC 60811 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 210 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 175 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 205 | °C | |
| Die Temperature | 215 | °C |
| Extrusion instructions |
|---|
| Crosslinking of the finished product is obtained by: Immersion of the bobbin in hot water at 85/90 °C for two hours (up to 3 mm thickness) Steam treatment at 0,15 bar for 5/6 hours. -Practically we suggest air crosslinking at natural temperatures and moisture: three or fivedays are enough. |
| Note Message | |
|---|---|
| 1 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Malen E FGAN 18-D003 | LyondellBasell Industries | LDPE | Malen |
| AXELERON™ GP C-0588 BK CPD | The Dow Chemical Company | LDPE | AXELERON™ |
| ISOTHANE® 1055D | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |
| Karina BLACK PVC COMPOUND 90850-48/ 1-D-AC-HSF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Deltron 3366 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PPS | Deltron |