XENOY™ X2420 resin
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IddroO_XENOY-X2420-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XENOYX2420 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and impact strength. X2420 has enhanced melt flowability, impact ductility and broad color space. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 265°C/2.16 kg | 12.0 | cm³/10min | |
| 300°C/1.2 kg | 26.0 | cm³/10min | |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.15 to 0.25 | % | |
| Across Flow : 3.20 mm | 0.30 to 0.40 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.020 | % | |
| Equilibrium, 23°C, 50% RH | 0.040 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3800 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 50.0 | MPa | ASTM D638 |
| Yield | 51.0 | MPa | ISO 527-2/5 |
| Break 3 | 35.0 | MPa | ASTM D638 |
| Break | 37.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Break | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(50.0 mm Span) | 3500 | MPa | ASTM D790 |
| Flexural Strength 6(Yield, 50.0 mm Span) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7 | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength 8 | ISO 179/1eU | ||
| -30°C | 95 | kJ/m² | |
| 23°C | 95 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D256 |
| -30°C 9 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 10 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| -30°C 11 | 74 | kJ/m² | ISO 180/1U |
| 23°C 12 | 110 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 36.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 111 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 101 | °C | |
| Vicat Softening Temperature | 118 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.400 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 105 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 255 to 290 | °C | |
| Front Temperature | 255 to 290 | °C | |
| Nozzle Temperature | 260 to 290 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-4344-0000 | Ravago Manufacturing Americas, LLC | PP Homopolymer | Ravago Compounds |
| MTEGRITY™ ABS AB305 | M. Holland Company | ABS | MTEGRITY™ ABS |
| Lupolen 1800 S | LyondellBasell Industries | LDPE | Lupolen |
| PLANAC BT-3500 | TOYOBO America, Inc. | PBT | PLANAC |
| Sylvin 4260-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |