XYRON™ TT520
| Category: | PPE+PP , Polyphenylene Ether + PP |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | XYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ida7n0_XYRON-TT520.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Modified PPE PP/PPE alloy 20% Filler Reinforced Dimensional stability Good |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(2.00 mm) | 0.70 to 0.90 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 40.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 20 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 64.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 6.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 120 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 65°C) | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x2 mm |
| 2 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ B70 G25 BK017S | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Geon™ Vinyl Flexible B87FB | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Generic UHMWPE | Generic | UHMWPE | Generic |
| HAIPLEN EP30 P15 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| KOPLA PC KBP1100 | KOPLA Co., Ltd. | PBT | KOPLA PC |