KetaSpire KT-880 CF30 is a high fluidity, 30% carbon fiber reinforced polyether ether ketone (PEEK). When the temperature is close to 300 ℃, the mechanical properties of carbon fiber reinforced KetaSpire PEEK reach the highest level in the industry and have the lowest linear thermal expansion coefficient of KetaSpire product series. KetaSpire PEEK is processed according to the highest industry standards and is characterized by various excellent properties, including excellent wear resistance, first-class fatigue resistance, easy melt processing, high purity, excellent resistance to organic matter, acids and alkalis and other chemicals. These characteristics make it very suitable for medical care, transportation, electronics, chemical processing and other industrial applications.

General Information
Filler / Reinforcement	Carbon fiber reinforced material, 30% filler by weight
Features	Good dimensional stability Electron beam disinfection Radiation disinfection Rigidity, high High strength Pressure cooker disinfection Good disinfection Ethylene oxide disinfection Anti-gamma radiation High liquidity Good chemical resistance Fatigue resistance Heat resistance, high Steam resistance thermal disinfection Disinfect with steam Flame retardancy
Uses	Films Pump parts Electrical/Electronic Applications Aircraft applications Industrial application Connector Seals Oil/Gas Supplies Surgical instruments Dental application field Medical/nursing supplies Medical equipment Medical devices
RoHS Compliance	Contact manufacturer
Appearance	Black
Forms	Particle
Processing Method	Machining Profile extrusion molding Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.45	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (400°C/5.0 kg)	50	g/10 min	ASTM D1238
PV Limit ¹	300000 - 400000	psi·fpm

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness	99		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
--	13500	MPa	ASTM D638
--	16000	MPa	ISO 527-2
Tensile Stress
Fracture	180	MPa	ISO 527-2
--	194	MPa	ASTM D638
Tensile Elongation
Fracture	1.8	%	ASTM D638
Fracture	1.7	%	ISO 527-2
Flexural Modulus
--	13500	MPa	ASTM D790
--	13200	MPa	ISO 178
Flexural Strength
--	280	MPa	ASTM D790
--	260	MPa	ISO 178
Compressive Strength	138	MPa	ASTM D695
Shear Strength	83.0	MPa	ASTM D732
Coefficient of Friction ²	0.28		ASTM D3702
Wear Factor (0.22 MPa, 4.1 m/sec)	46	10^-8 mm³/N·m	ASTM D3702

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact
--	68	J/m	ASTM D256
--	7.0	kJ/m²	ISO 180
Unnotched Izod Impact	530	J/m	ASTM D4812

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	147	°C	ISO 11357-2
Melting Temperature	343	°C	ISO 11357-3

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C, 1000 sec^-1)	150	Pa·s	ASTM D3835

Injection	Nominal Value	Unit
Drying Temperature	150	°C
Drying Time	4.0	hr
Rear Temperature	365	°C
Middle Temperature	370	°C
Front Temperature	375	°C
Nozzle Temperature	380	°C
Mold Temperature	175 - 205	°C
Injection Rate	Fast
Screw Compression Ratio	2.5:1.0 - 3.5:1.0

Note Message
1 .	GMW 16771-Sequence B
2 .	Dry

Resin Grade	Manufacturer	Category	Trademark
RTP 2100 TFE 5	RTP Company	PEI	RTP
Witcom HDPE AS-S-UV	Witcom Engineering Plastics B.V.	HDPE	Witcom HDPE
AIE PET 4010F	Asia International Enterprise (Hong Kong) Limited	PET	AIE PET
PLUSTEK PA360G6	Polyram Ram-On Industries	Nylon 66	PLUSTEK
Sylvin 8218-85 Green 3173	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin