ELIX™ Ultra HH 4115 HI
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ELIX Polymers, S. L. |
| Trademark: | ELIX™ Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IaFxZd_ELIX-Ultra-HH-4115-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELIX ULTRA HH 4115 HI Very high heat resistance ABS with extreme impact resistance ISO shortname: ISO 2580-1 ABS 2-X, MG, 115-15-35-20 Benefits:
Chemical Composition:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (25°C) | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow | 0.65 to 0.75 | % | |
| Flow | 0.65 to 0.75 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 42.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 7.0 | % | |
| Break, 23°C | 53 | % | |
| Nominal Tensile Strain at Break (23°C) | 20 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 2000 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 53 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 41 | kJ/m² | |
| 23°C | 58 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 113 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 113 | °C | ISO 306/B50 |
| -- | 115 | °C | ISO 306/B120 |
| CLTE - Flow (23 to 55°C) | 8.9E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4(2.00 mm) | < 40 | mm/min | ISO 3795 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Carbon Emission - Total (23°C) | < 25.0 | µgC/g | VDA 277 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | VDA 278 | ||
| FOG total : 23°C | < 5.00 | µg/g | |
| VOC total : 23°C | < 10.0 | µg/g |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Injection Velocity | 240 | mm/sec | ISO 294 |
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2 mm |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | US - FMVSS |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVASTER® B FRN 3 LS | Plastcom | PBT | SLOVASTER® |
| ZYLAR® 765 | INEOS Styrolution Group GmbH | MMBS | ZYLAR® |
| MXSTEN® CV77516 | Westlake Chemical Corporation | Plastomer | MXSTEN® |
| Appeel® 11D888 | DuPont Packaging & Industrial Polymers | EVA | Appeel® |
| Hostacom TRC 1193N | LyondellBasell Industries | TPO (POE) | Hostacom |