MOTIS™ LV Datasheet,PEEK,Invibio Inc.-SHANGHAI SUSHENG

MOTIS™ LV

Category:	PEEK , Polyetheretherketone
Manufacturer:	Invibio Inc.
Trademark:	MOTIS™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	IZszQ7_MOTIS-LV.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Combining versatility, strength, biocompatibility and superior material properties, MOTIS is a tool for innovation that drives device performance to the next level. At its core, MOTIS is an enhanced polyetheretherketone (PEEK) polymer with properties specifically developed for bearing applications against hard counterfaces, such as metal and ceramic. For device manufacturers, this means increased design flexibility and redefining what is possible. Superior biomaterials, in form and function, are more important than ever before. Until now, arthroplasty device design and performance have been bound by the limitations of existing metals, ceramics, and polymers, due to inherent characteristics (e.g. strength, stiffness), processing requirements, or performance limitations (e.g. wear, creep and fatigue properties). MOTIS overcomes many of these constraints - in both design and processing - by fundamentally redefining biomaterial properties and performance possibilities. To meet the critical demands of orthopedic joint arthroplasty, MOTIS utilizes carbon fiber technology to modify the performance characteristics of natural PEEK. MOTIS provides an inherently strong bond between fibers and matrix, with a fiber-to-matrix interfacial bond strength at least an order of magnitude stronger than UHMWPE and carbon fibers. Additionally, MOTIS has shown to be highly resistant to creep with less than 0.4% of creep measured under loads of 50MPa, maintaining implant shape and contact area under constant stress.

Message

Combining versatility, strength, biocompatibility and superior material properties, MOTIS is a tool for innovation that drives device performance to the next level. At its core, MOTIS is an enhanced polyetheretherketone (PEEK) polymer with properties specifically developed for bearing applications against hard counterfaces, such as metal and ceramic. For device manufacturers, this means increased design flexibility and redefining what is possible.

Superior biomaterials, in form and function, are more important than ever before. Until now, arthroplasty device design and performance have been bound by the limitations of existing metals, ceramics, and polymers, due to inherent characteristics (e.g. strength, stiffness), processing requirements, or performance limitations (e.g. wear, creep and fatigue properties).

MOTIS overcomes many of these constraints - in both design and processing - by fundamentally redefining biomaterial properties and performance possibilities.

To meet the critical demands of orthopedic joint arthroplasty, MOTIS utilizes carbon fiber technology to modify the performance characteristics of natural PEEK. MOTIS provides an inherently strong bond between fibers and matrix, with a fiber-to-matrix interfacial bond strength at least an order of magnitude stronger than UHMWPE and carbon fibers. Additionally, MOTIS has shown to be highly resistant to creep with less than 0.4% of creep measured under loads of 50MPa, maintaining implant shape and contact area under constant stress.

General Information
Features	Biocompatible Ethylene Oxide Sterilizable Fatigue Resistant Good Creep Resistance Good Dimensional Stability Good Flexibility Good Wear Resistance High Stiffness High Strength Radiation Sterilizable Radiotranslucent Steam Sterilizable
Uses	Body Implants Medical/Healthcare Applications
Agency Ratings	DMF Unspecified Rating FDA Unspecified Rating
Appearance	Black
Forms	Granules
Processing Method	Injection Molding Machining

Physical	Nominal Value	Unit	Test Method
Density	1.42	g/cm³	ISO 1183
Molding Shrinkage
Across Flow : 210°C	0.90	%
Flow : 210°C	0.10	%
Water Absorption (23°C, 24 hr)	0.50	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	105		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	15000	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Yield ¹	98.0	MPa
Yield	155	MPa
Tensile Strain			ISO 527-2
Break ²	2.8	%
Break	2.0	%
Flexural Modulus			ISO 178
-- ³	6400	MPa
--	12500	MPa
Flexural Stress			ISO 178
-- ⁴	164	MPa
--	230	MPa
Compressive Modulus	12000	MPa	ISO 604
Compressive Stress	200	MPa	ISO 604
Shear Modulus	2200	MPa	ISO 15310
Shear Strength	94.0	MPa	ASTM D732
Poisson's Ratio	0.41		ASTM E132

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength	5.5	kJ/m²	ISO 180
Unnotched Izod Impact Strength	30	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	343	°C
CLTE - Flow			ASTM D696
-- ⁵	1.2E-5	cm/cm/°C
-- ⁶	1.5E-5	cm/cm/°C

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity ⁷	3.70E-4	MPa	Internal Method

Note Message
1 .	Rod
2 .	Rod
3 .	Rod
4 .	Rod
5 .	Below Tg
6 .	Above Tg
7 .	Capillary Rheometer

Resin Grade	Manufacturer	Category	Trademark
Spartech Polycom SC7-7022R	Spartech Polycom	PC	Spartech
ACCUTECH™ HP0336W20L1	ACLO Compounders Inc.	PP Homopolymer	ACCUTECH™
Braskem PE TS7006	Braskem	LDPE	Braskem PE
Daplen™ EE108AE	Borealis AG	TPO	Daplen™
Sumiliteresin® PR-1070 I	SBHPP	Phenolic	Sumiliteresin®

Resin Grade

Manufacturer