Order Products : sales@su-jiao.com
Leona™ FG173
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IYyO9g_Leona-FG173.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ FG173 is a Polyamide 66 (Nylon 66) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Typical application: Electrical/Electronic Applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.65 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ||||
| Saturation, 23°C | -- | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | -- | 0.80 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | 60 | ASTM D785, ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11700 | 10500 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 174 | 137 | MPa | ISO 527-2 |
| -- | 167 | 142 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 2.5 | 3.5 | % | ASTM D638 |
| Break, 23°C | 2.0 | 2.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 10800 | 8300 | MPa | ASTM D790 |
| 23°C | 10300 | 8700 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 250 | 221 | MPa | ASTM D790 |
| 23°C | 259 | 188 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 29.0 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 11 | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 50 | 52 | kJ/m² | ISO 179 |
| Notched Izod Impact | 88 | 98 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 262 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 252 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | ||||
| -- | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 28 | -- | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 275 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVASTER® B1 GF 6 HML | Plastcom | PBT | SLOVASTER® |
| Sylvin 8437-76 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TRIBOCOMP® POM CF10 TS0 | EPIC Polymers | Acetal (POM) Copolymer | TRIBOCOMP® |
| DOW™ LLDPE DNDA-8335 NT 7 | The Dow Chemical Company | LLDPE | DOW™ LLDPE |
| OCTAL PET GS 05 | OCTAL Holding & Co. | PET | OCTAL PET |