KOPPS®S13A65BL is a polyphenylene sulfide (PPS) product, which contains a 65% filler. It is available in North America, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.95 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ISO 294-4 |
| Flow | 0.23 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.020 | % | ISO 62 |
| Balanced, 23°C, 60% RH | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 122 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 108 | MPa | ASTM D638 |
| 23°C | 130 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.0 | % | ASTM D638 |
| Fracture, 23°C | 1.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 16700 | MPa | ASTM D790 |
| 23°C | 16500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 186 | MPa | ASTM D790 |
| 23°C | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.35mm | 265 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 265 | °C | ISO 75-2/A |
| Melting Temperature | 285 | °C | ISO 11357-3, ASTM D3418 |
| CLTE - Flow | 2.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.00 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Comparative Tracking Index | 230 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 120 - 130 | °C | |
| Drying Time - Desiccant Dryer | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Nozzle Temperature | 300 - 320 | °C | |
| Mold Temperature | 120 - 140 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 202 HS | RTP Company | Nylon 66 | RTP |
| BESTDUR TPXG6/02 | Triesa Plastics | PBT+PET | BESTDUR |
| CERTENE™ PBM-18N | Muehlstein | PP Copolymer | CERTENE™ |
| Gallonprene® GP540-8505 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Kynar® 761A | Arkema | PVDF | Kynar® |