LNP™ STAT-LOY™ SLWM2105 compound
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IYB0gd_LNP-STAT-LOY-SLWM2105-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Anti-static PBT/PC blend, mineral 5% filled product |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/1.2 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 to 1.8 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2420 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield 2 | 46.5 | MPa | |
| Break 3 | 46.5 | MPa | |
| Tensile Elongation 4 | Internal Method | ||
| Yield | 20 | % | |
| Break | 20 | % | |
| Flexural Modulus 5(50.0 mm Span) | 2300 | MPa | ASTM D790 |
| Flexural Strength 6(Yield, 50.0 mm Span) | 77.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 41 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 161 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 9.0E+12 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 10 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titacon® SI902 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Geon™ Vinyl Rigid Extrusion L4230 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Epoxies, Ect. 50-3150 FR | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Sylvin 4200-80 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| POCAN® B 1205 XF 000000 | LANXESS Asia/Pacific | PBT | POCAN® |