Anjacom® 150-GF30
| Category: | PC , Polycarbonate |
| Manufacturer: | Almaak International GmbH |
| Trademark: | Anjacom® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IY7c1e_Anjacom-150-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Anjacom® 150-GF30 is a Polycarbonate (PC) material filled with 30% glass fiber. It is available in Europe for injection molding. Primary attribute of Anjacom® 150-GF30: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.43 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 5.00 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 125 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 146 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Glass Transition Temperature | 148 | °C | DSC |
| Vicat Softening Temperature | 148 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-1 | UL 94 | |
| Glow Wire Flammability Index (4.00 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Softell TKG 259N | LyondellBasell Industries | Polyolefin, Unspecified | Softell |
| TOTAL Polypropylene PPC 5571 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Karina STRAW PVC COMPOUND 750-38/ 14-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Perlast® G80A | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |
| Plaslube® PA6/6 CF30 TS12 BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |