Hostacom G3 N01 L
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IXMrWR_Hostacom-G3-N01-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hostacom" G3 N01 L is a 30% glass coupled PP homopolymer with low flow, very high stiffness and low CLTE. Low creep under load at elevated temperatures. The grade is not intended for medical, pharmaceutical or drinking water applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 230°C/2.16 kg | 1.00 | cm³/10min | |
| 230°C/5.0 kg | 5.00 | cm³/10min | |
| Molding Shrinkage | 0.30 to 1.0 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 110 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus - Secant | 5500 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 38 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 6.0 | kJ/m² | DIN 53453 |
| Unnotched Izod Impact Strength (23°C) | 22 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 160 | °C | ISO 306/A50 |
| -- | 130 | °C | ISO 306/B50 |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOND 3012 | SILON s.ro | LLDPE | TABOND |
| Zytel® 70G35HSL NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Delrin® SC655 NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Europrene Latice® 2430 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| IROCOAT® CA-237M | Huntsman Corporation | TPU, Unspecified | IROCOAT® |