Edistir® R 540E
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Edistir® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IWxMhz_Edistir-R-540E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIPS with high stiffness, matt surface finish and good heat resistance. Suitable for general extrusion of thick sheets and profiles. Also used for injection mouldings. Designation: Thermoplastics ISO 2897-PS-I,G,O93-O3-O7-18 Applications To be used in industrial panels for appliances and buildings. Injection moulding of shoe heels. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 24.0 | MPa | ISO 527-2/50 |
| Fracture | 29.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 60 | % | ISO 527-2/50 |
| Flexural Stress 1 | 43.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 100 | J/m | ISO 180/4A |
| -30°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 86.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 100 | °C | ISO 306/A50 |
| -- | 92.0 | °C | ISO 306/B50 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 7.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 65 | kV/mm | IEC 60243-1 |
| Dielectric Constant (50 Hz) | 2.50 | IEC 60250 | |
| Dissipation Factor (50 Hz) | 3.0E-4 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Designation | Thermoplastics ISO 2897-PS-I,G,093-03-07-18 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 20.0 - 60.0 | °C |
| Injection instructions |
|---|
| Predrying normally not required |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 - 240 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 700-SG5 | Toray Resin Company | ABS | Toyolac® |
| Vyncolit® 2920W | Vyncolit N.V. | Phenolic | Vyncolit® |
| Unichem 5811 | Colorite Polymers | PVC, Unspecified | Unichem |
| APEX® 82-E419A-2 | Teknor Apex Company | PVC, Flexible | APEX® |
| Sylvin 9657-85 Clear Red 6264 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |