LNP™ THERMOCOMP™ AB002 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IUWE1b_LNP-THERMOCOMP-AB002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP AB002 is a compound based on ABS resin containing 10% Glass Bead. Also known as: LNP* THERMOCOMP* Compound AB-1002 Product reorder name: AB002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.11 | g/cm³ | ISO 1183 |
| -- | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.80 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.22 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.36 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 35.0 | MPa | ASTM D638 |
| Yield | 34.0 | MPa | ISO 527-2/5 |
| Break 3 | 32.0 | MPa | ASTM D638 |
| Break | 30.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.3 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2/5 |
| Break 5 | 29 | % | ASTM D638 |
| Break | 24 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2590 | MPa | ASTM D790 |
| -- 7 | 2420 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 60.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 64.0 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 63.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 10 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 560 | J/m | ASTM D4812 |
| 23°C 11 | 34 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.0 | J | ASTM D3763 |
| -- | 2.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 93.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 92.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 81.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 79.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBB2751 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| VESTOLIT® P 1382 K | VESTOLIT GmbH & Co. KG | PVC, Unspecified | VESTOLIT® |
| TRIREX® Compound 3025G20 | Samyang Corporation | PC | TRIREX® Compound |
| ULTEM™ HU2210 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Elvax® 760 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |