RAMSHINE PV701
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMSHINE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ISeHPn_RAMSHINE-PV701.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UV STABILIZIED ABS FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 | % | ASTM D955 |
| -- | 0.40 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.30 | % | ASTM D570 |
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2150 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 45.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 35 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 2000 | MPa | ASTM D790 |
| -- | 200 | MPa | ISO 178 |
| Flexural Strength | 65.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D256 |
| 23°C | 25 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 84.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525, ISO 306 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 205 - 220 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® AZ 200 Natural | Radici Plastics | Nylon 66 | Radilon® |
| ADDILENE H 520 T40 | ADDIPLAST | PP Homopolymer | ADDILENE |
| Chiao Fu PP PP212GM30 NAT | Chiao Fu Enterprises Co., Ltd. | PP, Unspecified | Chiao Fu PP |
| Di-Pak™ R-4528/30 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| LEXAN™ ML2010 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |