Ebalta AH 120 / TL
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ISZx8p_Ebalta-AH-120-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta AH 120/TL is a very thin liquid epoxy resin with high values of strength and dimensional stability. Due to its good impregnating and wetting properties it is suitable as laminating resin for high-strength components with fabrics of glass -or carbon fiber. ebalta AH 120/TL is suitable for laminating of thin as well as thick laminates with large surface up to a thickness of 20 mm. A post-curing should be executed, if possible before demoulding. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 84 - 88 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 3050 - 3550 | MPa | ISO 178 |
| Flexural Stress | 115 - 135 | MPa | ISO 178 |
| Compressive Stress | 97.0 - 117 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 45 - 55 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 95.0 - 101 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 25 | ||
| Post Cure Time | |||
| 60°C | 6.0 - 8.0 | hr | |
| 90°C | 3.0 - 5.0 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.09 - 1.13 | g/cm³ | |
| Viscosity (25°C) | 0.70 - 0.90 | Pa·s | |
| Curing Time (20°C) | 18 - 24 | hr | |
| Pot Life 1(20°C) | 80 - 90 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA6 A1RG7301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6 | Shandong PA6 |
| Utomer UT380 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| Laprene® 8K1000A80 | SO.F.TER. SPA | SEBS | Laprene® |
| LUVOCOM® 19-7277 VP | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| Sylvin 6185-80 White 1379 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |