Ecomass® 1080ZD92
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Ecomass Technologies |
| Trademark: | Ecomass® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ISKpgW_Ecomass-1080ZD92.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ecomass®1080ZD92 is a polyamide material that contains a tungsten filler. This product is available in North America and is processed by injection molding. Ecomass®The main features of 1080ZD92 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 7.98 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6580 | MPa | ASTM D638 |
| Tensile Strength | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.1 | % | ASTM D638 |
| Flexural Modulus | 4650 | MPa | ASTM D790 |
| Flexural Strength | 49.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 121 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 107 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 0.21 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 73.9 | °C | |
| Drying Time - Desiccant Dryer | 4.0 | hr | |
| Processing (Melt) Temp | 204 - 254 | °C | |
| Mold Temperature | 57.2 - 85.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.103 - 0.172 | MPa | |
| Screw Speed | 100 - 250 | rpm | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 6.35 - 12.7 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Pack (Hold) Pressure: 65 to 75% of Injection PressureFill Time: 1.0 to 2.0 in/secPack (Hold) Time: 10 to 15 secCooling Time: As requiredFeed Throat: CooledNozzle Type: Reverse TaperCheck Type: Free FlowMaximum Drying Temp: 200 °FDryer Dew Point: -20 to -40 °FMinimum Air Flow: 0.8 to 1.0 CFMInjection Pressure: As Required |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sorona® 3030GV NC010 | DuPont Performance Polymers | PTT | Sorona® |
| TAIRILAC AF3500 | Formosa Plastics Corporation | ABS | TAIRILAC |
| Delrin® PC691 NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| LNP™ THERMOCOMP™ 4X08423 compound | SABIC Innovative Plastics | PFA | LNP™ THERMOCOMP™ |
| Sylvin 8950-70FU Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |