LNP™ THERMOCOMP™ RF008XXZ compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ISCcSH_LNP-THERMOCOMP-RF008XXZ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* RF008XXZ is a compound based on Nylon 66 resin containing 40% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound RF-1008 Product reorder name: RF008XXZ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.48 | g/cm³ | ASTM D792 |
| -- | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 1.3 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.28 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.60 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.97 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13300 | MPa | ASTM D638 |
| -- | 12200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 185 | MPa | ASTM D638 |
| Break | 189 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.5 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10400 | MPa | ASTM D790 |
| -- | 12100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 275 | MPa | ASTM D790 |
| -- | 287 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 3 | 74 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.3 | J | ASTM D3763 |
| -- | 3.08 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 253 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | > 240 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 5.8E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 5.9E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-HO-20GF | Pro Polymers | PP Homopolymer | Pro-Comp™ |
| Scolefin 13 T 10-0 | Ravago Group | PP Homopolymer | Scolefin |
| Borealis PP BE50-7032 | Borealis AG | PP Homopolymer | Borealis PP |
| Karina STRAW PVC COMPOUND 800-38/39-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hifax CB 1160 G1 1646 | LyondellBasell Industries | PP Copolymer | Hifax |