MAGNUM™ 3325 MT
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IRlC8E_MAGNUM-3325-MT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM™ 3325 MT is a resin with excellent processing characteristics and a matt surface finish. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processablility with a stable light base colour that is ideal for self-colouring. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| -- | 1.05 | g/cm³ | ISO 1183/B |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 2.5 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 10 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 to 0.70 | % | ASTM D955 |
| -- | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| 3.20 mm, Injection Molded | 2200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield 2 | 42.3 | MPa | ASTM D638 |
| Yield, 3.20 mm, Injection Molded | 43.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield, 3.20 mm, Injection Molded | 3.3 | % | ISO 527-2/50 |
| Break 3 | 25 | % | ASTM D638 |
| Flexural Modulus | |||
| -- 4 | 2210 | MPa | ASTM D790 |
| 3.20 mm, Injection Molded | 2100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 5 | 64.5 | MPa | ASTM D790 |
| 3.20 mm, Injection Molded | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C, Compression Molded | 8.0 | kJ/m² | ISO 179/2 |
| -30°C, Injection Molded | 11 | kJ/m² | ISO 179/1eA |
| 23°C, Injection Molded | 17 | kJ/m² | ISO 179/1eA |
| 23°C, Compression Molded | 12 | kJ/m² | ISO 179/2 |
| Notched Izod Impact | |||
| 23°C, 3.20 mm 6 | 310 | J/m | ASTM D256 |
| -30°C | 10 | kJ/m² | ISO 180/1A |
| 23°C | 17 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact 7 | ASTM D3763 | ||
| -29°C, 3.20 mm, Peak Energy | 31.7 | J | |
| -29°C, 3.20 mm, Total Energy | 34.3 | J | |
| 23°C, 3.20 mm, Peak Energy | 31.1 | J | |
| 23°C, 3.20 mm, Total Energy | 45.4 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 96.1 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 82.8 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ASTM D1525 |
| -- | 102 | °C | ISO 306/B50 |
| CLTE - Flow | 9.4E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 8(2.00 mm) | 60 | mm/min | ISO 3795 |
| Flame Rating 9 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Carbon Emission 10 | 20.0 | µg/g | VDA 277 |
| Fogging 11(100°C) | 98 | % | ISO 6452 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 5.1 mm/min |
| 5 . | Type I, 5.1 mm/min |
| 6 . | 0.25 mm Notch Depth |
| 7 . | 3.39 m/sec |
| 8 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 9 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 10 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 11 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 8083 | Colorite Polymers | PVC, Unspecified | Unichem |
| AVALON® 95 AB | Huntsman Corporation | TPU-Polyester | AVALON® |
| DENILUB Z 30G 3TF | Vamp Tech | PPA | DENILUB |
| Gallonprene® GP210-4502L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Elastron® V V101.D51.B | Elastron USA, Inc. | TPV | Elastron® V |