VENYL SN000 - 3121
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IQPtih_VENYL-SN000---3121.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SN000 - 3121 is a standard coloured polyamide 6 intended for Injection moulding. APPLICATIONS VENYL SN000 - 3121 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL SN000 - 3121 is available in both yellow (VENYL SN000 - 3121) but other colours can be provided on request. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.50 to 1.5 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.8 to 3.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (L-Scale) | 100 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 85.0 | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 50 | 200 | % | ISO 527-2 |
| Flexural Modulus | 2700 | 900 | MPa | ISO 178 |
| Flexural Stress | 130 | 65.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | 40 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 | |
| Notched Izod Impact | 50 | 150 | J/m | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 170 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 240 to 255 | °C | |
| Nozzle Temperature | 220 to 265 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 70.0 to 90.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 to 60.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-7810 | Quantum Composites Inc. | Polyester, TS | Quantum Composites |
| Next Nylon 66 Prime Series PG30-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| ACCUTECH™ CP0437M10L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Alpha PVC 2212-100 CLEAR 0003 | AlphaGary | PVC, Semi-Rigid | Alpha PVC |
| BUPLEN® 9531 | LUKOIL Bulgaria Ltd. | PP Copolymer | BUPLEN® |