Nypol® PA A3 G50 HS UV RH PRTA011 NR416
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IPOxyY_Nypol-PA-A3-G50-HS-UV-RH-PRTA011-NR416.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 in black color reinforced with 50% of fiberglass, heat stabilized, resistance to hydrolysis and UV. Good set of thermal properties, electrical and mechanical. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.56 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.1 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % | |
| Ash Content | 48 to 52 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16800 | 12900 | MPa | ISO 527-2/2 |
| Tensile Stress | ||||
| Yield | 250 | 200 | MPa | ISO 527-2/2 |
| Break | 260 | 205 | MPa | ISO 527-2/1/5 |
| Tensile Strain (Break) | 2.7 | 3.5 | % | ISO 527-2/2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 16 | 15 | kJ/m² | |
| 23°C | 17 | 19 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | 95 | kJ/m² | |
| 23°C | 110 | 120 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 18 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (-30°C) | 15 | 15 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 262 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 257 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 254 | -- | °C | ISO 306/B |
| Melting Temperature (DSC) | 250 to 265 | -- | °C | ISO 3146 |
| CLTE | ASTM E831 | |||
| Flow | 1.4E-5 | -- | cm/cm/°C | |
| Transverse | 7.2E-5 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 285 to 295 | °C | |
| Mold Temperature | 100 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEOFLON™ EC-6510 | DAIKIN AMERICA, INC. | ETFE | NEOFLON™ |
| ADENE NFQAL | A.D. Compound spa | PP Homopolymer | ADENE |
| Elastron® G G100.A50.N | Elastron USA, Inc. | SEBS | Elastron® G |
| EnCom PPE-PS 190-55 | EnCom, Inc. | PPE+PS | EnCom |
| Karina CLEAR PVC COMPOUND 75/201-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |