VECTRA® S475
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | INxweM_VECTRA-S475.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Super High Flow, High heat Resistance and Low Warp for Thin Parts. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 in natural and black at 0.15mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electricals 130°C, mechanicals 130°C. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.37 | % | ISO 294-4 |
| Flow direction | 0.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 180 | MPa | ISO 178 |
| Flexural Strain at Break | 2.4 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 305 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 213 | °C | ISO 75-2/C |
| Melting Temperature 1 | 350 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity | |||
| 1 MHz | 3.70 | IEC 60250 | |
| 2.05 GHz | 4.15 | Internal method | |
| Dissipation Factor | |||
| 1 MHz | 8.0E-3 | IEC 60250 | |
| 2.05 GHz | 1.0E-3 | Internal method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 40.0 | °C | |
| Rear Temperature | 330 - 350 | °C | |
| Middle Temperature | 340 - 360 | °C | |
| Front Temperature | 345 - 365 | °C | |
| Nozzle Temperature | 355 - 370 | °C | |
| Processing (Melt) Temp | 360 - 375 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 355 to 370°CZone 4 Temperature: 355 to 370°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalene® 556 | Lion Copolymer, LLC | EPDM | Royalene® |
| Silmar® SIL94BA-1575 | Interplastic Corporation | Polyester, TS | Silmar® |
| Ultrason® E KR 4113 | BASF Corporation | PESU | Ultrason® E |
| AKROMID® B3 5 FR natural (3520) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| IROCOAT® CA-237 | Huntsman Corporation | TPU, Unspecified | IROCOAT® |