LNP™ LUBRICOMP™ DL003P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | INQiKm_LNPLUBRICOMPDL003Pcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Exceptional Processing. Also known as: LNP* LUBRICOMP* Compound DL-4030 EP Product reorder name: DL003P |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.90 - 1.1 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.90 - 1.1 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.70 - 0.90 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.17 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2430 | MPa | ASTM D638 |
| -- | 2340 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 51.7 | MPa | ASTM D638 |
| Yield | 53.0 | MPa | ISO 527-2 |
| Fracture | 42.7 | MPa | ASTM D638 |
| Fracture | 42.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.2 | % | ASTM D638 |
| Yield | 5.3 | % | ISO 527-2 |
| Fracture | 40 | % | ASTM D638 |
| Fracture | 23 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2100 | MPa | ASTM D790 |
| -- | 2020 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 82.7 | MPa | ASTM D790 |
| -- | 83.8 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.18 | ASTM D3702 Modified | |
| With Self-Static | 0.070 | ASTM D3702 Modified | |
| Wear Factor - Washer | 60.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 30.3 | J | ASTM D3763 |
| -- | 72.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 122 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 121 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 1.8 | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| ESTASAN SAN 2000 | Cossa Polimeri S.r.l. | SAN | ESTASAN |
| Eltex® A3180PN1852 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| Epolene® C-16 | Westlake Chemical Corporation | LDPE | Epolene® |
| HiFill® PA6 GF50 L | Techmer Engineered Solutions | Nylon 6 | HiFill® |